Techmer ES Plastiblend® PA6 NAT001 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Nucleated |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® PA6 NAT001 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Good Processability and High FlowAppearance: NaturalTPCI# 1327102Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.6 % @Time 86400 sec |
1.6 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 3.17 mm |
0.014 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 74.5 MPa | 10800 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 3.17 mm |
1.70 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 108 µm/m-°C | 60.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 57.2 °C | 135 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP6NR PC (Asia Pacific)
- Resinlab® AR 4305 HP Metal Bonding Methacrylate Adhesive
- Flint Hills 44S2A Polypropylene Impact Copolymer
- Mitsui Arlenâ„¢ A350 50% Glass Fiber-Reinforced Modified Nylon 6T (COND)
- SABIC Innovative Plastics LNP STAT-KON MD000 PP
- BASF Ultramid® A3HG5 25% Glass Filled PA66 (Dry)
- SABIC Innovative Plastics LNP THERMOTUF VX99810 Super Tough Nylon
- Arkema Group Oroglas® V 045 Acrylic, Extrusion Grade (discontinued **)
Copyright © lookpolymers.com All Rights Reserved