- Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone
Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Techmer ES |
| Trade Name | Plaslube® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plaslube® J-50/10/SI/2 Polycarbonate, 10% GFR, 2% Silicone.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 165 Plate & Rolled Bar; AT (TF00) Temper; All Thicknesses (UNS C17000)
- Momentive Performance Materials IS808 Translucent Adhesive Sealant, General Purpose Paste
- Styron CALIBREâ„¢ 2061-22 Polycarbonate Resin
- Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR
- Vyncolit X6952 Novolac Phenolic
- Cytec Conathane® CC-1194 (Conap) Polyurethane Dielectric Conformal Coating
- 3M FM0234R2 Clear Polyester Label Products
- Johnson Matthey Argo-braze 40N Silver Brazing Alloy for Tungsten Carbide Brazing
Copyright © lookpolymers.com All Rights Reserved