SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin

Category Polymer , Thermoplastic , Polyolefin , Polyphenylene Ether/PPO
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL WCV065 PPE+Polyolefin.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Flexible, non-halogenated FR, PPE+Polyolefin resin designed for evaluation in Automotive ISO6722 Class A-C applications.
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Melt Flow 20.2 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 20.2 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D1238
Melt Index of Compound 20 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 20 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 65
65
30S reading; ASTM D2240
Tensile Strength at Break 37.0 MPa
5370 psi
Type I, 50 mm/min; ASTM D638
37.0 MPa
5370 psi
50 mm/min; ISO 527
Tensile Strength, Yield 37.0 MPa
5370 psi
Type I, 50 mm/min; ASTM D638
39.0 MPa
5660 psi
50 mm/min; ISO 527
Elongation at Break 38 %
38 %
50 mm/min; ISO 527
45 %
45 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 17 %
17 %
50 mm/min; ISO 527
37 %
37 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.45 GPa
210 ksi
1 mm/min; ISO 527
Flexural Yield Strength 41.0 MPa
5950 psi
1.3 mm/min, 50 mm span; ASTM D790
44.0 MPa
6380 psi
2 mm/min; ISO 178
Flexural Modulus 1.15 GPa
167 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.26 GPa
183 ksi
2 mm/min; ISO 178
Izod Impact, Notched 5.50 J/cm
10.3 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 4.30 J/cm²
20.5 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 33.0 J

@Temperature 23.0 °C
 24.3 ft-lb

@Temperature 73.4 °F
 ASTM D3763
42.0 J

@Temperature -30.0 °C
 31.0 ft-lb

@Temperature -22.0 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 131 µm/m-°C

@Temperature -40.0 - 40.0 °C
 72.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 115 °C

@Thickness 3.20 mm
 239 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 93.0 °C
199 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
84.0 °C

@Thickness 3.20 mm
 183 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 71.0 °C
160 °F
Rate B/50; ASTM D1525
71.0 °C
160 °F
Rate B/50; ISO 306
76.0 °C
169 °F
Rate B/120; ISO 306
Electrical Properties Metric English Comments
Dielectric Constant 2.5

@Frequency 1.00e+6 Hz
 2.5

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
 0.0020

@Frequency 1.00e+6 Hz
 IEC 60250