ExxonMobil HDPE HTA 001HD High Density Polyethylene (HMW) Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Exxon Chemical
Trade Name HDPE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil HDPE HTA 001HD High Density Polyethylene (HMW) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HTA 001HD is a high weight HDPE film grade. Films made from HTA 001HD exhibit excellent impact and toughness properties as well as high stiffness. Availability: Africa & Middle East and Asia Pacific Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: Blown FilmGrocery SacksLinersProduce BagsProduce Bags on a RollRefuse BagsThin Gauged Consumer BagsTrash Can LinersInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D4883
Melt Flow 9.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
9.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 40.7 MPa
5900 psi
ASTM D882
Film Tensile Strength at Yield, TD 30.3 MPa
4400 psi
ASTM D882
Film Elongation at Break, MD 220 %
220 %
ASTM D882
Film Elongation at Break, TD 430 %
430 %
ASTM D882
Elmendorf Tear Strength MD 8.0 g
8.0 g
ASTM D1922
Elmendorf Tear Strength TD 30 g
30 g
ASTM D1922
Dart Drop Test 190 g
0.419 lb
ASTM D1709A
Film Tensile Strength at Break, MD 59.3 MPa
8600 psi
ASTM D882
Film Tensile Strength at Break, TD 55.8 MPa
8100 psi
ASTM D882
1% Secant Modulus, MD 1170 MPa
170000 psi
ASTM D882
1% Secant Modulus, TD 1170 MPa
170000 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C
259 °F
ASTM D1525