SABIC Innovative Plastics LNP LUBRICOMP RX88514 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RX88514 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). AddedLNP LUBRICOMP* RX85514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.610 % | 0.610 % | 50% RH, 24 hrs; ASTM D570 |
| 0.930 % | 0.930 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527 |
| 79.0 MPa | 11500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 7.2 % | 7.2 % | Type I, 5 mm/min; ASTM D638 |
| 7.4 % | 7.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.3 % | 7.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | 50 mm/min; ASTM D638 |
| 3.82 GPa | 554 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 |
| Flexural Modulus | 3.32 GPa | 482 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 3.56 GPa | 516 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.16 J/cm | 9.67 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.38 | 0.38 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm³/N-M | 3.00 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
42.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 228 °C | 442 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9620 F Ceramic Bodies
- Nilit FRIANYL A63 GV20 Nylon 6.6 for injection molding, 20% glass fiber reinforced
- Polymer Resources NY66-G33-[color]H Nylon, 33% Glass Reinforced, Heat Stabilized (DAM)
- IDI Composites 44-10 MW Thermoset Polyester, Molding
- GRECO ISOPAK 640 Polycarbonate/ABS Alloy
- GRECO ISOTHANE 5090A Polyether TPU Resin
- Teknor Apex MONPRENE® MP 2850M Thermoplastic Elastomer
- Arlon 18976XA023 Silicone Rubber/Fiberglass Laminate
- Asahi Kasei Leona® 14G33 33% Glass Filled Nylon 66
- Haynes 25 alloy, room temperature after 20% cold reduction, 1120°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved