- Techmer ES Luriblend® PA6/6 CF33 ML2 BK 33% Carbon Filled
Techmer ES Luriblend® PA6/6 CF33 ML2 BK 33% Carbon Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PA6/6 CF33 ML2 BK 33% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 33% Filler by WeightAdditive: Molybdenum Disulfide LubricantFeatures: Lubricated, Low Friction and Good Wear ResistanceAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ASTM D792 |
| Water Absorption | 0.48 % @Time 86400 sec |
0.48 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength, Yield | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 303 MPa | 44000 psi | ASTM D790 |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.17 mm |
1.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | ASTM D1894 |
| Coefficient of Friction, Static | 0.12 | 0.12 | ASTM D1894 |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C | 10.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 200 ohm | 100 - 200 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 FRM 1 PA6, flame retardant
- Michelman® Michem® Emulsion 91735 Nonionic polypropylene emulsion
- SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10
- Schott GG495 Long Pass Filter
- Taiwan Sheen Soon Sheenthane® A9720 Thermoplastic Polyurethane Elastomer
- Borealis BL0521 High Density Polyethylene
- Tra-Con Tra-Bond FS443 Color Keyed Thixotropic Epoxy Adhesive
- Chicago Extruded Metals UNS C38000 Copper-Zinc-Lead Alloy
- ExxonMobil Optema® TC-114 Cast Ethylene Methyl Acrylate
Copyright © lookpolymers.com All Rights Reserved