Techmer ES HiFill® PP 0142 B Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Techmer ES HiFill® PP 0142 B Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Unspecified Filler/ReinforInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % <br>@Time 86400 sec |
0.050 % <br>@Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm <br>@Thickness 3.17 mm |
0.015 in/in <br>@Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 12 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
12 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 35.9 MPa | 5200 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm <br>@Thickness 3.17 mm |
0.500 ft-lb/in <br>@Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.2 µm/m-°C | 19.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 107 °C | 225 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.8 °C | 145 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90215 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kolon SPESIN® KP213G15SIBL Glass Fiber Reinforced PBT Compound Resin
- Lotte Chemical Titan TITANLENE® LDI300YY Low density polyethylene resin
- H.C. Starck Pure Molybdenum CLC, Arc-Cast Bar
- Solvay Specialty Polymers Ryton® R-4-222NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Unifrax Fiberfrax® Vari-Form™ B Casting Mix
- Zotefoams Plastazote® LD24FMSV Low Density Polyethylene Foam, Flame Retarded
- Polimeri Europa SINKRAL D160 ABS, Heat Stabilized (discontinued **)
Copyright © lookpolymers.com All Rights Reserved