- Techmer ES HiFill® HIPS GF30 30% Glass Filled
Techmer ES HiFill® HIPS GF30 30% Glass Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Grade, Glass Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HIPS GF30 30% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsGlass Fiber Reinforcement, 30% Filler by WeightAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 3.17 mm |
0.0015 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 7.24 GPa | 1050 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 2.14 J/cm @Thickness 3.17 mm |
4.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.6 µm/m-°C | 17.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 503RS PC (Europe-Africa-Middle East)
- Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin T650-35-6K-UC309-5HS Carbon Fabric
- PolyOne Edgetek® PS-30CF/000 HF UV BLACK Polybutylene Terephthalate (PBT)
- Kingfa FRHIPS-1162 Flame Retardant Polystyrene
- LTL Color Compounds ColorRxâ„¢ PE2-0201A Antimicrobial HDPE
- Solvay Chemicals Ixper® 35M Magnesium Peroxide
- Techmer ES Plaslube® J-1/30/TF/13/SI/2 NAT PA66
- A. Schulman POLYBATCH™ Light Grey LL803366/4 Concentrate Based In LLDPE
- Fainplast Compounds PG 58/1AT Flexible PVC, Extrusion Modified with Rubber
- DuPont Performance Polymers Zytel® 80G14AHS NC010 Nylon 66 (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved