Techmer ES HiFill® HIPS 484 GY
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HIPS 484 GY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAppearance: GreyInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 38.6 MPa | 5600 psi | ASTM D790 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.20 µm/m-°C | 4.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.2 °C | 189 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs PT487 Pt(C2H8N2)2Cl2 Bis(ethylenediamine)platinum(II) chloride
- Precision Polymer Engineering N50M Nitrile Rubber
- MarkeTech WCu20 Tungsten Copper Alloy
- Karina E 830-18/99-CRM Gray PVC Compound
- Dow Corning XIAMETER® PMCPOFX-8803 Fluid
- Eurostar Staramide RF00AES PA66/6, 50% Glass Filled, Injection Molded
- Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced
- Alliance BIN-45 Bonded (Composite) Magnetic Material
- Asahi Kasei Thermylon® LSG-440A-H 60% Ceramic and Glass Fiber Reinforced, Heat
- Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)
Copyright © lookpolymers.com All Rights Reserved