Total 2285 HDPE Bimodal Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total 2285 HDPE Bimodal Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: T-shirt sacks, trash can liners, merchandise bags, multi-wall liner, deli wrapInformation provided provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D 792 |
| Water Vapor Transmission | 12.4 g/m²/day | 0.799 g/100 in²/day | 100°F; E 96/66 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.080 g/10 min @Load 2.16 kg |
0.080 g/10 min @Load 4.76 lb |
ASTM D 1238 |
| 0.32 g/10 min @Load 5.00 kg |
0.32 g/10 min @Load 11.0 lb |
ASTM D 1238 | |
| High Load Melt Index | 11 g/10 min @Load 21.6 kg |
11 g/10 min @Load 47.6 lb |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 36.5 MPa | >= 5300 psi | ASTM D 882 A |
| Film Tensile Strength at Yield, TD | >= 34.5 MPa | >= 5000 psi | ASTM D 882 A |
| Film Elongation at Break, MD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Film Elongation at Break, TD | 300 - 500 % | 300 - 500 % | ASTM D 882 A |
| Secant Modulus, MD | 0.841 GPa | 122 ksi | ASTM D 882 A |
| Secant Modulus, TD | 0.910 GPa | 132 ksi | ASTM D 882 A |
| Elmendorf Tear Strength MD | 24 g | 24 g | ASTM D 1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D 1922 |
| Dart Drop Test | 350 g | 0.772 lb | ASTM D 1709 |
| Film Tensile Strength at Break, MD | >= 63.4 MPa | >= 9200 psi | ASTM D 882 A |
| Film Tensile Strength at Break, TD | >= 67.6 MPa | >= 9800 psi | ASTM D 882 A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 127 °C | 260 °F | ASTM D3417 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Process | Film | |
| Region | US & Canada | Bamberger Polymers Distribution |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V72H Fluoroelastomer Compound
- Saint-Gobain Meldin® 2211 Bearing
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.001" thick)
- Total PPH 9099 Polypropylene, Homopolymer
- TPI Porene® ABS-SR101 High Impact Extrusion Grade ABS Resin
- Ensinger TECATEC™ CF60 Polyaryletherketone (PAEK)
- Arkema Group Pebax® MV 1041 SN 01 Polyether Block Amide (PEBA) (Dry)
- Braskem PCD 0440 HECO Polypropylene Heterophasic Copolymer
- 3M Scotchcal™ IJ5000 Reflective Graphic Film'
- SABIC Innovative Plastics ULTEM 9076 PEI (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved