Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AFA-6133 V0 Z Polyphthalamide (PPA), 33% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® AFA-6133 V0 Z is a 33% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Electrical Properties; Good Stiffness; High Flow; High Strength; Hot Water MoldabilityUses: Automotive Applications; Automotive Electronics; Bobbins; Connectors; Electrical/Electronic ApplicationsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D6779 PA104G35; GM GMW15702 Color: BK BlackInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 199 MPa | 28900 psi | ASTM D638 |
| Tensile Strength, Yield | 63.4 MPa @Temperature 175 °C |
9200 psi @Temperature 347 °F |
4; ISO 527-2 |
| 75.2 MPa @Temperature 150 °C |
10900 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 114 MPa @Temperature 100 °C |
16500 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 186 MPa @Temperature 23.0 °C |
27000 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| 1.6 % @Temperature 23.0 °C |
1.6 % @Temperature 73.4 °F |
ISO 527-2 | |
| 2.4 % @Temperature 100 °C |
2.4 % @Temperature 212 °F |
ISO 527-2 | |
| 4.9 % @Temperature 175 °C |
4.9 % @Temperature 347 °F |
ISO 527-2 | |
| 5.1 % @Temperature 150 °C |
5.1 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 16.1 GPa | 2340 ksi | ASTM D638 |
| 5.10 GPa @Temperature 175 °C |
740 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 5.93 GPa @Temperature 150 °C |
860 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 9.17 GPa @Temperature 100 °C |
1330 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 14.5 GPa @Temperature 23.0 °C |
2100 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 224 MPa | 32500 psi | ASTM D790 |
| 87.6 MPa @Temperature 175 °C |
12700 psi @Temperature 347 °F |
4; ISO 178 | |
| 101 MPa @Temperature 150 °C |
14600 psi @Temperature 302 °F |
4; ISO 178 | |
| 161 MPa @Temperature 100 °C |
23400 psi @Temperature 212 °F |
4; ISO 178 | |
| 259 MPa @Temperature 23.0 °C |
37600 psi @Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| 4.62 GPa @Temperature 175 °C |
670 ksi @Temperature 347 °F |
ISO 178 | |
| 4.96 GPa @Temperature 150 °C |
719 ksi @Temperature 302 °F |
ISO 178 | |
| 8.07 GPa @Temperature 100 °C |
1170 ksi @Temperature 212 °F |
ISO 178 | |
| 12.6 GPa @Temperature 23.0 °C |
1830 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 145 MPa | 21000 psi | ASTM D695 |
| Shear Strength | 80.0 MPa | 11600 psi | ASTM D732 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.90 J/cm | 12.9 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.20 kJ/m² | 3.90 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 4.60 J/cm² | 21.9 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.00 µm/m-°C @Temperature 100 - 200 °C |
3.89 µin/in-°F @Temperature 212 - 392 °F |
2 |
| 17.0 µm/m-°C @Temperature 0.000 - 100 °C |
9.44 µin/in-°F @Temperature 32.0 - 212 °F |
2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature 0.000 - 100 °C |
35.6 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 110 µm/m-°C @Temperature 100 - 200 °C |
61.1 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 310 °C | 590 °F | ASTM D3418 |
| 310 °C | 590 °F | ISO 11357-3 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Annealed; ASTM D648 |
| 282 °C | 540 °F | Unannealed; Flatwise; ISO 75-2/A | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 |
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz |
4.1 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 4.4 @Frequency 60.0 Hz |
4.4 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 24.0 kV/mm @Thickness 3.20 mm |
610 kV/in @Thickness 0.126 in |
ASTM D149 |
| Dissipation Factor | 0.011 @Frequency 1.00e+6 Hz |
0.011 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | PLC 1; UL 746 |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746 |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 327 - 332 °C | 621 - 630 °F | |
| Middle Barrel Temperature | 316 - 324 °C | 601 - 615 °F | |
| Front Barrel Temperature | 316 - 324 °C | 601 - 615 °F | |
| Melt Temperature | 321 - 338 °C | 610 - 640 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | <= 120 °C @Time 14400 sec |
<= 248 °F @Time 4.00 hour |
|
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Suggested Max |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Flame Retardant | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Part Marking Code | >PA6T/66-GF33< | ISO 11469 |
| Processing Technique | Water-Heated Mold Injection Molding | |
| Resin ID | PA6T/66 GF33 FR(17) | ISO 1043 |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Latrobe LSSâ„¢ 17-4 Precipitation Hardening Stainless Steel (ASTM Type 360)
- KKPC KOSYN 1507 Styrene Butadiene Rubber
- SABIC Innovative Plastics LNP STAT-KON AE002 ABS (Asia Pacific)
- Shin-Etsu Silicones KE-5551U High Strength Silicone Elastomer
- SABIC Innovative Plastics LNP THERMOTUF MF004AI PP
- Polyram RamTal PM7013G2 Acetal, 10% Glass Fiber
- Lubrizol ESTANE® 54640 Ether Based Thermoplastic Polyurethane (European Grade)
- Lubrizol ESTANE® 58144 Ether Based Thermoplastic Polyurethane (European Grade)
- CPC - Vycom CELTEC® Expanded Rigid foam PVC board
Copyright © lookpolymers.com All Rights Reserved