Techmer ES HiFill FR® PPO/HIPS MM20 IM FR 20% Mineral Filled

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass + Mineral Filler
Manufacturer	Techmer ES
Trade Name	HiFill FR®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES HiFill FR® PPO/HIPS MM20 IM FR 20% Mineral Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 20% Filler by WeightAdditive: Impact Modifier Features: Flame Retardant and Impact ModifiedInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in³	ASTM D792
Water Absorption	0.060 % @Time 86400 sec	0.060 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0060 cm/cm @Thickness 3.17 mm	0.0060 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	106	106	ASTM D785
Tensile Strength, Yield	65.5 MPa	9500 psi	ASTM D638
Elongation at Break	8.0 %	8.0 %	ASTM D638
Flexural Yield Strength	103 MPa	15000 psi	ASTM D790
Flexural Modulus	2.96 GPa	430 ksi	ASTM D790
Izod Impact, Notched	1.33 J/cm @Thickness 3.17 mm	2.50 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	36.0 µm/m-°C	20.0 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	98.3 °C	209 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.3 °C	200 °F	Unannealed; ASTM D648
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm	1.00e+17 ohm-cm	ASTM D257
Dielectric Strength	17.7 kV/mm	450 kV/in	Method A (Short-Time); ASTM D149