Phillips Sumika Marlex® CHP-035 Thermoplastic Polyolefin (discontinued **)

Category	Polymer , Thermoplastic , Polyolefin
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Phillips Sumika Marlex® CHP-035 Thermoplastic Polyolefin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Applications: Painted air-bag coversSoft interior trimSoft touch overmoldingInformation provided by Chevron Phillips.Phillips Sumika Polypropylene Company has been shut down, as announced in 2011.

Physical Properties	Metric	English	Comments
Density	0.899 g/cc	0.0325 lb/in³	Injection molded specimen; ASTM D1505
Melt Flow	9.0 g/10 min @Load 2.16 kg, Temperature 230 °C	9.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	93	93	Injection molded specimen; ASTM D2240
Tensile Strength, Yield	13.0 MPa	1890 psi	20 in/min, injection molded, type 1 specimen; ASTM D638
Flexural Modulus	0.240 GPa	34.8 ksi	Injection molded specimen, 0.05 in/min, Tangent method; ASTM D790
Izod Impact, Notched	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	injection molded specimen; ASTM D256
Impact Test	30.5 J @Temperature -40.0 °C	22.5 ft-lb @Temperature -40.0 °F	Instrumented, 15 mph; ASTM 3763
Tear Strength	87.0 kN/m	496 pli	Die C, 2 in/min; D1004

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	52.0 °C	126 °F	injection molded specimen; ASTM D648