PolyOne Edgetek® AM-30CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced (discontinued **)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® AM-30CF/000 Polyphthalamide (PPA), Carbon Fiber Reinforced
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Carbon Fiber ReinforcedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.30 % | 0.30 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0015 cm/cm | 0.0010 - 0.0015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 228 MPa | 33000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 26.9 GPa | 3900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 331 MPa | 48000 psi | ASTM D790 |
| Flexural Modulus | 26.9 GPa | 3900 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.00 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.10 µm/m-°C @Temperature 20.0 °C |
4.50 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.793 W/m-K | >= 5.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 304 °C | 580 °F | Annealed, 0.125 in bars; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 1000 ohm-cm | 10 - 1000 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | Molding |
| Mold Temperature | >= 135 °C | >= 275 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Precision Polymer Engineering B60B Styrene Butadiene Rubber
- SABIC Innovative Plastics GELOY CR8510 ASA
- Polymer Resources PC-IM4 Polycarbonate, Impact Modified, Easy Flow
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- A. Schulman CP878-01 Natural Linear, Low-Density Polyethylene
- Hexcel® HexWeb® HRP/F35 - 2.5 Nonmetallic Flex-Core Honeycomb
- UBE UBESTA® 3035UF Rigid Piping Grade Nylon 12
- CP-Polymer-Technik Wellamid® 6000 HWUVCP Nylon 6, UV Stabilized, Heat Stabilized, Conditioned
- Asahi Glass Lumiflon FE-4200 Solvent Soluble Fluoropolymer
- A. Schulman POLYBATCH™ Light Grey 80426U Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved