Techmer ES HiFill FR® PA6 GF33 FR HS L BK065 33% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | HiFill FR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill FR® PA6 GF33 FR HS L BK065 33% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Flame Retardant, Heat Stabilized and Lubricated Appearance: BlackTPCI# 6536102Information provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 |
| Water Absorption | 0.75 % @Time 86400 sec |
0.75 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 149 MPa | 21600 psi | ASTM D638 |
| Elongation at Break | 3.1 % | 3.1 % | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 3.17 mm |
1.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm @Thickness 3.17 mm |
16.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.6 µm/m-°C | 12.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746 |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL746 |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | UL746 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs CU110 Cu(C2H3O2)2 Copper(II) acetate, anhydrous
- SABIC CC862 High Density Polyethylene for Injection Molding
- Abatron AboCast 7802-1/AboCure 50-11 Epoxy (discontinued **)
- Indium Corp. Indalloy® 84001 Flux #1 Paste Flux containing Ammonium Chloride
- LG Chemical Methyl Acrylate
- Sekisui PIOCELAN LSP-20DB Moldable Polymer Foam
- Total HDPE SB 1359 High Density Polyethylene - Injection Stretch Blow Molding
- ExxonMobil 512 Mobilgard 12 Series
- BASF Ultradur B 4300 G6 LS High Speed BK15045 30% Glass Filled PBT
- 3M AP596 Adhesion Promoter
Copyright © lookpolymers.com All Rights Reserved