ExxonMobil Label-Lyte™ 50LL210 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 50LL210 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: An uncoated biaxially oriented, transparent polypropylene film for Pressure Sensitive labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Good gloss and transparencyGood printability on the treated sideGood moisture resistanceRecommended for in-line top coatingApplications: Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral WatersBiscuits/Cookie/Crackers Dairy ProductsDry Foods and Beverage PowdersHealth and Beauty CareHousehold and DetergentsIndustrial Uses: Pressure Sensitive LabelsProcessing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing, UV Letterpress Printing, UV Offset Lithography Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 50.8 microns | 2.00 mil | ExxonMobil Method |
| Coating Weight | 44.8 g/m² | 28.0 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 65 % | 65 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 120 MPa | 17400 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 245 MPa | 35500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % @Temperature 135 °C, Time 432 sec |
4.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 2.0 % @Temperature 135 °C, Time 432 sec |
2.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.7 % | 1.7 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 15500 in2/lb |
Users viewing this material also viewed the following:
- Nabaltec GRANALOX® NM 9922 B Ceramic Body, Binder Free
- Fiberfil® J-60/10/E/M Polypropylene Homopolymer, 10% Glass Reinforced, Chemically coupled
- Saint-Gobain Chemfab® q-GUARD® 18 Insulation Jacketing
- Total PPR 8650 Polypropylene, Random Copolymer
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/40%/285T2/AS4C-6K
- Dow SPECTRIM™ MM 310-B Polyol
- Asahi Kasei Thermylon® NSG-440A-H 60% Ceramic and Glass Fiber Reinforced
- Ineos ABS Triax® DP 3155 ABS + Polyamide Blend (Conditioned) (discontinued **)
- BASF Ultraform® N2644 Z9 POM + PUR
Copyright © lookpolymers.com All Rights Reserved