- Techmer ES Electrafil® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed
Techmer ES Electrafil® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber Reinforced, PTFE Lubricated
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 207 MPa | 30000 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| Flexural Yield Strength | 296 MPa | 43000 psi | ASTM D790 |
| Flexural Modulus | 17.9 GPa | 2600 ksi | ASTM D790 |
| Compressive Yield Strength | 138 MPa | 20000 psi | ASTM D256 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.4 µm/m-°C @Temperature 20.0 °C |
8.00 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00 - 10.0 ohm-cm | 1.00 - 10.0 ohm-cm | ASTM C611 |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D4496 |
Users viewing this material also viewed the following:
- PolyOne Trilliant™ HC THC-02 1200 IL Natural Polyamide 66 (Nylon 66)
- Kazanorgsintez Polyethyleneglycol-68
- Lehmann & Voss LUVOCOM® 19-8263 Polyamide 46, with carbon fiber and glass fiber, lubricant modified
- LG Chemical LUMID HI2152A(W) PA6+GF15%, High Impact
- Lotus Nano Paint NAP 301 Airport Nano-paint
- A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE
- CTC X-PRO TF 1020 GP Polypropylene Homopolymer, 20% Talc Filled
- 3M Scotch-Seal™ 2084 Metal Sealant
- Asahi Glass ASAHIKLIN AK-225G Hydrochlorofluorocarbon Solvent
- BASF Ultramid® B32 0.015 BOPA Film
Copyright © lookpolymers.com All Rights Reserved