Unitika TERRAMAC HV-6250H Polylactic Acid (PLA)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | Unitika |
| Trade Name | TERRAMAC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika TERRAMAC HV-6250H Polylactic Acid (PLA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Foam, Extrusion, blow, and foam sheet grades. Bio-based materials produced from annually renewable raw materials.Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Melt Flow | 1.0 - 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 - 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 |
| Flexural Strength | 111 MPa | 16100 psi | ISO 178 |
| Flexural Modulus | 4.70 GPa | 682 ksi | ISO 178 |
| Charpy Impact, Notched | 0.190 J/cm² | 0.904 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 120 °C | 248 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 200 °C | 356 - 392 °F | |
| Middle Barrel Temperature | 190 - 230 °C | 374 - 446 °F | |
| Front Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Die Temperature | 20.0 - 120 °C | 68.0 - 248 °F | Vacuum and pressure molding |
| 150 - 180 °C | 302 - 356 °F | Foam extrusion molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Opaque white |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1890T PC Copolymer (Europe-Africa-Middle East)
- LATI LARPEEK 10 G/30 30% Glass Reinforced Polyetheretherketone (PEEK) (Unverified Data**)
- Chevron Phillips HiD® 9035 HDPE Injection Molding Resin (discontinued **)
- Permabond 798 Cyanoacrylate, Surface insensitive
- SABIC Innovative Plastics LNP THERMOCOMP EF006 PEI
- Polyplastics Duranex® 2002 Polybutylene Terephthalate (PBT), Low friction, Low wear
- Hexcel® HexPly® M18 356°F (180°C) Curing Epoxy Matrix
- Master Bond Supreme 33 High Temperature Resistant, Structural Adhesive
- DuPont Performance Polymers Minlon® IG38C1 BK434 Nylon 66 (Unverified Data**)
- Techmer ES Electrablend® PC SS15 15% Stainless Steel Filled
Copyright © lookpolymers.com All Rights Reserved