Techmer ES Elastoblend® PA6 GF34 IM HS 34% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 GF34 IM HS 34% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 34% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 172 MPa | 25000 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 0.862 GPa | 125 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.20 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.35 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
4.40 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.9 J/cm @Thickness 3.17 mm |
26.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8502 EXCEL GREY
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.5 PHR Sulfur
- Lucas-Milhaupt FOS FLO 7 Copper Phosphorus Alloy
- Shinkong Synthetic Fibers Shinite® T101G30 PET, 30% Glass Filled
- A. Schulman LP390-01 Narrow Molecular Weight Copolymer
- Esstech X-863-0070 Surface Active Monomer, NTG-GMA, Magnesium Salt, C32H40N2O10Mg
- Aclo Accutech Polypropylene Homopolymer HP0336W10L1 Wollastonite Reinforced
- Braskem Pluris 9300 LLDPE Blown Film Extrusion Polyethylene Quatropolymer
- Ametek AM 388™ Alloy (UNS C72650) TB00 Solution HT
- Carpenter Gall-Tough PLUS™ Stainless, Annealed, 25% Cold Work
Copyright © lookpolymers.com All Rights Reserved