EPICHEM Epiblend PC/ABS nero Polycarbonate/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | EPICHEM srl |
| Trade Name | Epiblend |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM Epiblend PC/ABS nero Polycarbonate/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.22 % @Temperature 23.0 °C |
0.22 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Index of Compound | 20 - 30 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 - 30 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238, ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638, ISO R527 |
| Elongation at Break | 80 % | 80 % | ASTM D638, ISO R527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | >= 3.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 5.62 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | >= 100 °C | >= 212 °F | BS 3456, IEC 335 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | >= 120 °C @Load 5.00 kg |
>= 248 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| >= 130 °C @Load 0.999 kg |
>= 266 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 - 750 °C @Thickness 3.20 mm |
1200 - 1380 °F @Thickness 0.126 in |
VDE 0471/P2-4, IEC 695 |
| 650 - 750 °C @Thickness 2.00 mm |
1200 - 1380 °F @Thickness 0.0787 in |
VDE 0471/P2-4, IEC 695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.0 @Frequency 1000 Hz |
3.0 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 250 V | 250 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- 3M Dyneon™ Fluorel™ FC-2182 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- PolyOne Edgetek® PS-30GF/000 FR V0 Polybutylene Terephthalate (PBT), Glass Filled (discontinued **)
- M. Holland Company LD120 LDPE (discontinued **)
- SPS Guang Zhou SAMATâ„¢ 5000A Flame-retarded Polypropylene
- Tipco Tipcolene® FPC 10 - 10% Calcium Carbonate Reinforced Polypropylene Homopolymer
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- 3M FM00G Indoor UL Recognized Clear Polyester Overlaminate Label Product
- PolyOne Stat-Tech™ AS-30GF/000 SD Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- Adell BJ-17 Nylon 6, 35% Glass Reinforced; High Impact
Copyright © lookpolymers.com All Rights Reserved