ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin (discontinued **)
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 29.5 % | 29.5 % | ExxonMobil Method |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 8.48 MPa | 1230 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 2.69 MPa | 390 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 330 % | 330 % | ASTM D882 |
| Film Elongation at Break, TD | 880 % | 880 % | ASTM D882 |
| Film Elongation at Yield, MD | 19.4 % | 19.4 % | ASTM D882 |
| Film Elongation at Yield, TD | 9.5 % | 9.5 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 0.197 g/micron | 5.00 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.06 g/micron | 230 g/mil | ASTM D1922 |
| Dart Drop | 3.94 g/micron | 100 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 31.9 MPa | 4630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
| 1% Secant Modulus, MD | 36.3 MPa | 5270 psi | ASTM D882 |
| 1% Secant Modulus, TD | 35.2 MPa | 5100 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 71.1 °C | 160 °F | Peak Melting Temperature; ExxonMobil Method |
| Vicat Softening Point | 46.1 °C | 115 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Gloss | 73 % | 73 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® 4701-30-30 Cellular Urethane Foam
- SABIC Innovative Plastics Cycoloy® MC5303 PC+ABS (Asia Pacific)
- Haynes Hastelloy® C-22HS™ Nickel Alloy Plate and Bar, Hot-rolled, Solution Annealed
- Solvay ALKAMULS® STO-UNBL Surfactant
- Saint-Gobain COHRlastic® 9255 High Performance Silicone Solid Rubber
- Teknor Apex Telcar® TL-1000-105UV Thermoplastic Elastomer
- Chase Plastics CP Pryme® NN213GL (COND, 50% RH) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated
- Goodfellow Copper 90/Titanium 10 Alloy
- Buckeye Polymers BP PP 0015 R Blk Reprocessed Polypropylene, Unfilled
- Bhansali Engineering Abstron HI-34 ABS High Impact Injection Molding
Copyright © lookpolymers.com All Rights Reserved