Techmer ES Elastoblend® PA6 GF30 IM HS L 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 GF30 IM HS L 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Impact Modifier Features: Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % @Time 86400 sec |
1.5 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0012 cm/cm @Thickness 3.17 mm |
0.0012 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 145 MPa | 21100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 234 MPa | 34000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.92 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.60 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.9 J/cm @Thickness 3.17 mm |
26.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+12 ohm-cm | 2.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S65E Silicone Rubber
- Mar-Bal MB1000-25 Thermoset Polyester Composite Molding Compound
- SABIC Innovative Plastics LNP STAT-KON JX89626 PES
- Borealis Borstar® FB2310 LLDPE for Film
- Dow Corning Z-1216 PHENYLTRICHLOROSILANE
- DuPont Performance Polymers Crastin® S600F10 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Eurotec® Tecomid® NB40 NL IH PA 6 impact modified
- American Computer Optics Low -Medium Transmission Filter 3 mm
- Latrobe DuraTech™ A11 Powder Metal Tool Steel (AISI A11)
Copyright © lookpolymers.com All Rights Reserved