Supreme Petrochem SP 6520 Permanent Antistatic Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 6520 Permanent Antistatic Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics No sloughing Fully colorable Meets MIL-PRF-81705D static decay specification Functions even in low humidity levels Processing Injection molding Extrusion & Forming Applications Component handling systems Chip trays ESD applications PCB boxes Component boxes Material Status: Commercial : ActiveAgency Ratings: Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 27.0 MPa | 3920 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 43.1 MPa @Thickness 3.20 mm |
6250 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.47 GPa @Thickness 3.20 mm |
213 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.20 mm |
1.03 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 98.0 °C | 208 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 - 1.00e+10 ohm-cm | 1.00e+9 - 1.00e+10 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+9 - 1.00e+10 ohm | 1.00e+9 - 1.00e+10 ohm | ASTM D257 |
| Static Decay | <= 2.0 sec | <= 2.0 sec | MIL-PRF-81705D |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 230 °C | <= 446 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | ( 2 hrs) Pre drying temp. |
Users viewing this material also viewed the following:
- Okulen® 1000 PE-UHMW, Multi-color
- PTS Tristar® PC-10FR-(V16) 16 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Indium Corp. Indalloy 87 Indium-Tin Solder Alloy
- Karina 6122/23-RTR Kariprene Crepe
- Techmer ES HiFill® POM CO 0167 S1 LE Acetal
- Styrolution PS 476L HIPS
- SABIC Innovative Plastics Noryl EBN90 PPE+HIPS (Asia Pacific)
- Polyram RamTough PZ305G4 Polycarbonate, 20% Glass Fiber
- BASF Diisopropanolamine 90% Solution
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N774 Filler
Copyright © lookpolymers.com All Rights Reserved