Supreme Petrochem SP 553 Flame Retardant Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Flame Retardant |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SP 553 Flame Retardant Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics High flow properties Good balance of toughness and rigidity Available in any color Processing MoldingApplications Large size T.V. Cabinets VCR cabinets Electrical boxes, electrical appliance partsMaterial Status: Commercial : ActiveAgency Ratings: UL 94 file E 185934Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.5 MPa | 3550 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 39.2 MPa @Thickness 3.20 mm |
5690 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.20 mm |
270 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm @Thickness 3.20 mm |
1.87 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 82.0 °C | 180 °F | IEC335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C | 1560 °F | IEC 695-2-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 93 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 93 |
| Dielectric Constant | 2.6 @Frequency 1e+6 Hz |
2.6 @Frequency 1e+6 Hz |
IEC 250 |
| Dissipation Factor | 0.00040 @Frequency 1e+6 Hz |
0.00040 @Frequency 1e+6 Hz |
IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 250 °C | <= 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Pre drying temp. |
Users viewing this material also viewed the following:
- Mytex Polymers AS319L-01US Thermoplastic Polyolefin, 19% Talc Filled
- Kleerdex Vinyloy™ 100 Acrylic/PVC Thermoplastic Sheet (discontinued **)
- DSM Somos® 8110 Epoxy Photopolymer (discontinued **)
- H.C. Starck Amperit® 583.2 Chromium Carbide-Nickel 83-17 (Cr3C2-Ni)
- SGL Carbon Group SIGRAFIL C® C25 S006 EPY Staple Carbon Fiber, Epoxy Sizing
- DSM Arnitel® UM552 55 Shore D Copolyester Elastomer (North America)
- 3M SJ5400 Protective Product, Molded Shapes
- Karina E 841-08/184-Y-ERYB Beige PVC Compound
Copyright © lookpolymers.com All Rights Reserved