Supreme Petrochem SC 6501 Toughened Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Supreme Petrochem LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Supreme Petrochem SC 6501 Toughened Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics Excellent melt strength Extremely tough Easy printability Easy miscibility with most grades of polystyrene Processing Extrusion Thermoforming Injection MoldingApplications Impact modifier for HIPS for industrial thermoforming Toys, appliances requiring very high toughness Material Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 200 °C |
10 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 14.7 MPa | 2130 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | >= 75 % | >= 75 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 17.2 MPa @Thickness 3.20 mm |
2490 psi @Thickness 0.126 in |
ASTM D790 |
| Flexural Modulus | 0.686 GPa @Thickness 3.20 mm |
99.6 ksi @Thickness 0.126 in |
ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm @Thickness 3.20 mm |
7.49 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | 1kg / 120°C; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 220 °C | <= 428 °F | |
| Mold Temperature | 40.0 - 50.0 °C | 104 - 122 °F |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 81 T 30 PP, 30% mineral filling
- DuPont™ Sclairfilm® LX-3 LLDPE Film, Laminating, 50.8 µm Thickness (discontinued **)
- Kolon NOPLA® KE131 PEN-PET Copolyester
- SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Europe-Africa-Middle East)
- PlastxWorld CEVIAN® E80 ABS
- A. Schulman POLYFLAM™ RPP 1360 Non-Halogenated Homopolymer Polypropylene
- Covestro Baydur® 660 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System
- DuPont Teijin Films Mylar® LB Polyester Film, 75 Gauge (19 µm)
- Colorite Polymers 3511-02 General Purpose Vinyl Compound
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
Copyright © lookpolymers.com All Rights Reserved