Sumitomo Bakelite Sumikon® PM-9640 Glass Filled Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled |
| Manufacturer | Sumitomo Bakelite High Peformance Plastics |
| Trade Name | Sumikon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite Sumikon® PM-9640 Glass Filled Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Two stage glass fiber filled black phenolic. It is especially designed for applications requiring high strength and dimensional stability with excellent heat resistance. PM-9640 is widely used in automotive applications. Typical applications include motor housings, brush holders, and heat insulators. Plasticities available for transfer, and injection molding.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.770 g/cc | 0.0278 lb/in³ | ASTM D1895 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 120 | 120 | |
| Tensile Strength, Ultimate | 138 MPa | 20000 psi | ASTM D638 |
| Tensile Modulus | 18.6 GPa | 2700 ksi | ASTM D638 |
| Flexural Strength | 227 MPa | 32900 psi | ASTM D790 |
| Compressive Strength | 289 MPa | 41900 psi | ASTM D695 |
| Izod Impact, Notched | 0.400 J/cm | 0.749 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 24.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
13.3 µin/in-°F @Temperature 73.4 - 140 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C | 302 °F | |
| Flammability, UL94 | V-1 @Thickness 0.800 mm |
V-1 @Thickness 0.0315 in |
|
| V-1 @Thickness 0.800 mm |
V-1 @Thickness 0.0315 in |
||
| V-0 @Thickness 6.00 mm |
V-0 @Thickness 0.236 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.3 @Frequency 1e+6 Hz |
4.3 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 15.7 kV/mm | 399 kV/in | Step by step; ASTM D149 |
| 17.7 kV/mm | 450 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 12.0 Month | 12.0 Month |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PE 6250D (506H4) High Density Polyethylene
- A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene
- Hexcel® HexForce™ 3743 Fiber Glass Fabric
- A. Schulman PP 828S-01 Polypropylene Medium Impact Molding Grade Polypropylene
- Braskem GM7746CA HDPE Blow Molding Polyethylene
- BASF Neopolen® P 8220 K 0.03 g/cc Core density; Expanded Polypropylene (Europe)
- Bulk Molding Compounds BMC 700 Thermoset Polyester, High Arc Quench Electrical Grade
- SYNTHOS Krasten® 562E High Impact Polystyrene
- Arkema Group LOTRYL® 17 BA 07 Copolymer Ethylene - Butyl Acrylate
Copyright © lookpolymers.com All Rights Reserved