Sumitomo Bakelite North America 2004B Glass Reinforced Hardware Grade Epoxy
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America 2004B Glass Reinforced Hardware Grade Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Epoxy is the premier material for military firewall connectors.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.00 g/cc | 0.0723 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 48 hours, 50°C. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | Compression Molding. ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Barcol | 72 | 72 | |
| Tensile Strength, Ultimate | 62.0 MPa | 8990 psi | ASTM D638 |
| Flexural Yield Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 33.0 µm/m-°C @Temperature 20.0 °C |
18.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.607 W/m-K | 4.21 BTU-in/hr-ft²-°F | ASTM F433 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | ASTM D648A |
| UL RTI, Electrical | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| UL RTI, Mechanical without Impact | 130 °C | 266 °F | UL temperature Index, UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | >= 50 % | >= 50 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.0 | 4.0 | Wet; ASTM D150 |
| Dielectric Strength | 11.0 kV/mm | 279 kV/in | Wet, short term. ASTM D149 |
| Dissipation Factor | 0.019 @Frequency 1e+6 Hz |
0.019 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| Arc Resistance | 170 sec | 170 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 143 - 177 °C | 289 - 351 °F | compression/transfer molding. |
| 174 - 182 °C | 345 - 360 °F | injection molding. |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 81 T 20 PP, 20% mineral filling
- PolyOne Bergamid™ AB700 UF Polyamide 66/6 Copolymer (Nylon 66/6)
- LNP Stat-Kon® EC-1008 EM BK8-115 Polyetherimide, Carbon Fiber Reinforcement (discontinued **)
- Freudenberg Simrit SC1210 S310 Silicone Elastomer
- Struktol STRUKSILON 8118 Silicone Stabilizer for PU Foam
- Tra-Con Tra-Bond 2125NB Repair Epoxy Adhesive
- Cresset Powers Cress-Alon™ NF3040 4% Nano Clay Loaded, 3.0 r.v. Film Grade Nylon 6, Dry As Molded
- DuPont Performance Polymers Neoprene WD Polychloroprene Rubber
- Arlon 51970R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Dow LDPE 607A Low Density Polyethylene, High Clarity Blown Film Grade
Copyright © lookpolymers.com All Rights Reserved