Styron Pulse® 2000EZ PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 2000EZ PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Engineering ResinInformation provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ISO 1183 B |
| Water Absorption | 0.15 % | 0.15 % | 23°C, 24hrs; ISO 62 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294 |
| Melt Flow | 24 g/10 min @Load 5.00 kg, Temperature 260 °C |
24 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527-2 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ISO 527-2 |
| Elongation at Break | 90 % | 90 % | ISO 527-2 |
| Elongation at Yield | 4.5 % | 4.5 % | ISO 527-2 |
| Tensile Modulus | 2.33 GPa | 338 ksi | ISO 527-2 |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 47.0 kJ/m² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
ISO 180-4A |
| 63.0 kJ/m² @Temperature 23.0 °C |
30.0 ft-lb/in² @Temperature 73.4 °F |
ISO 180-4A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | unannealed; ISO 75-A |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | unannealed; ISO 75-A |
| Vicat Softening Point | 129 °C | 264 °F | 5Kg / 50°C/hr; ISO 306B |
| 142 °C | 288 °F | 1Kg / 120°C/hr; ISO 306A |
Users viewing this material also viewed the following:
- Outokumpu 4438 High Performance Austenitic Stainless Steel
- DuPont™ Sclairfilm® LWS-2 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **)
- Fujipoly Industries Sarcon® 45H Thin-Film HR
- SABIC Innovative Plastics LNP STAT-KON DE003ER PC (Asia Pacific)
- Styron XZ 94462.01 Carboxylated SB
- Teknor Apex Monprene® MP 1755L3 Thermoplastic Elastomer
- Diamond Polymers ABS 3300
- Dow SE BR-1202D Stereospecific high cis-1,4 Polybutadiene (BR)
- Fainplast Compounds GS 69/PL Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved