Styron Magnumâ„¢ 8325 ABS, Sheet Coextrusion Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Sheet |
| Manufacturer | Styron |
| Trade Name | Magnum™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Magnumâ„¢ 8325 ABS, Sheet Coextrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resin are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming.MAGNUM® 8325 ABS resin is a low gloss sheet coextrusion grade.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM Data |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |
| Melt Flow | 2.6 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.6 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | ASTM Data |
| Tensile Strength, Yield | 37.2 MPa | 5400 psi | ASTM Data |
| Elongation at Break | 100 % | 100 % | ASTM Data |
| Elongation at Yield | 2.6 % | 2.6 % | ISO Data |
| Tensile Modulus | 1.83 GPa | 265 ksi | ASTM Data |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM Data |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO Data, Low Temp |
| 2.20 J/cm² | 10.5 ft-lb/in² | ISO Data | |
| Impact Test | 46.0 J @Temperature 23.0 °C |
33.9 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.0 µm/m-°C @Temperature 20.0 °C |
43.9 µin/in-°F @Temperature 68.0 °F |
ISO data |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.0 °C | 174 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 107 °C | 225 °F | |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
Users viewing this material also viewed the following:
- Radici Radilon® A ESL128 (cond.) Nylon 66
- DuPont Bynel® 41E689 Adhesive Resin (discontinued **)
- Momentive Performance Materials HCM Boron Nitride (BN) Powder
- CoorsTek Epoxy Seal 216 (ES-216) B-staged epoxy lids
- DSM Stanyl® TW441 (COND) Nylon 46 High Viscosity, Heat Stabilized, Lubricated (North America)
- Chosun Refractories COD-2 Special brick
- Eurotec® Tecomid® NA40 GB30 NL HS PA6.6, 30% glass bead reinforced, heat stabilized, natural
- BASF Ultramid® B3EG6 LS BK 23189 30% Glass Filled PA6 (Conditioned)
- Braskem Green PE SLL118 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene
- Plaslok 306 Black General Purpose Mineral/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved