Styron EMERGEâ„¢ 7600 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 7600 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: EMERGEâ„¢ PC/ABS 7600 is an ignition-resistant PC/ABS blend that contains no chlorine or bromine additives. It combines the superior physical properties of PC & the excellent processability of ABS, resulting in high toughness and high flow. This resin is suitable for use in a wide range of applications. EMERGE PC/ABS 7600 Natural has undergone biocompatibility testing based on ISO 10993 (Parts 5 & 10) and is suitable for use in medical equipment housings.Main Characteristics: Ignition-ResistantChlorine and Bromine FreeISO 10993 (Parts 5 & 10)Applications:Medical equipment housingsInformation technology equipmentConsumer electronicsOffice and business equipmentRetail sales equipmentInformation provided by Styron
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 19 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 19 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118

@Thickness 3.20 mm
 118

@Thickness 0.126 in
 Injection Molded; ASTM D785
Tensile Strength at Break 44.1 MPa

@Thickness 3.20 mm
 6400 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Strength, Yield 55.2 MPa

@Thickness 3.20 mm
 8010 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Break 80 %

@Thickness 3.20 mm
 80 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Yield 4.0 %

@Thickness 3.20 mm
 4.0 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Modulus 2.69 GPa

@Thickness 3.20 mm
 390 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Flexural Strength 88.9 MPa

@Thickness 3.20 mm
 12900 psi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Flexural Modulus 2.83 GPa

@Thickness 3.20 mm
 410 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Izod Impact, Notched 5.90 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 11.1 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Thermal Properties Metric English Comments
Hot Ball Pressure Test 87.2 °C
189 °F
IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C

@Thickness 3.20 mm
 190 °F

@Thickness 0.126 in
 Unannealed, Injection Molded; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 77.2 °C

@Thickness 3.20 mm
 171 °F

@Thickness 0.126 in
 Unannealed, Injection Molded; ASTM D648
Vicat Softening Point 102 °C

@Load 1.02 kg
 216 °F

@Load 2.25 lb
 Rate B (120°C/h); ASTM D1525
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
Oxygen Index 31 %
31 %
ASTM D2863
Glow Wire Test 825 °C

@Thickness 2.00 mm
 1520 °F

@Thickness 0.0787 in
 Ignition; IEC 60695-2-13
950 °C

@Thickness 2.00 mm
 1740 °F

@Thickness 0.0787 in
 Index; IEC 60695-2-12
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F
Aim
216 - 241 °C
421 - 466 °F
Mold Temperature 60.0 - 71.1 °C
140 - 160 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour