| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Extrusion Grade |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PP H Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.010 % @Temperature 23.0 °C |
0.010 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Deformation | 0.48 % @Time 86400 sec, Pressure 100 MPa |
0.48 % @Time 24.0 hour, Pressure 14500 psi |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 | 70 | DIN 53505 |
| Tensile Strength at Break | 38.5 MPa | 5580 psi | ISO 527 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527 |
| Elongation at Break | 80 % | 80 % | ISO 527 |
| Elongation at Yield | 8.0 % | 8.0 % | ISO 527 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ISO 527 |
| Compressive Yield Strength | 12.0 MPa @Strain 1.00 % |
1740 psi @Strain 1.00 % |
ISO 604 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 105 µm/m-°C | 58.3 µin/in-°F | ASTM D696 |
| 140 µm/m-°C @Temperature 23.0 - 100 °C |
77.8 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 | |
| Maximum Service Temperature, Air | 100 °C | 212 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ISO 75 |
| Vicat Softening Point | 94.0 °C | 201 °F | ISO 306 |
| Minimum Service Temperature, Air | 0.000 °C | 32.0 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.3 @Frequency 1.00e+6 Hz |
2.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Loss Index | 0.00020 @Frequency 1.00e+6 Hz |
0.00020 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Light Gray | |
| UV Resistance | N |
Users viewing this material also viewed the following:
- Polymer Resources PC/ABS-GP1-[color]-UV General Purpose PC/ABS Alloy, UV-stabilized
- Pau Tai UNISTAB EC-198 Stabilizers for Cable
- SABIC Innovative Plastics Lexan® SLX2432T PC Copolymer (Asia Pacific)
- SABIC Innovative Plastics LNP FARADEX DS0036I PC
- I. Stern 750 Medium Impact Black ABS
- Elgiloy® Co-Cr-Ni Alloy, Strip, 20% Cold Reduction, Heat Treated
- Colorite Polymers 8511G-015 (Extrustion), 8512G-015 (Molding) Radiation Sterilizable Vinyl Compound
- Dymax 9-20525 HGA and OHGA Disk Drive Adhesive
- Aleris HOGAL 5558 Aluminum 5026-O/H111
- ExxonMobil 600 W Mobil Cylinder Oil
Copyright © lookpolymers.com All Rights Reserved