CP-Polymer-Technik Wellamid® 6000 CF 18 HWCP 18% Carbon Fiber Nylon 6, Heat Stabilized, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 CF 18 HWCP 18% Carbon Fiber Nylon 6, Heat Stabilized, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.0 - 2.5 % | 2.0 - 2.5 % | 23°C/50%RH; DIN 53495 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 4.00 mm |
0.0030 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 4.00 mm |
0.0090 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 |
| Flexural Modulus | 11.5 GPa | 1670 ksi | DIN 52457 |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 176 °F |
DIN 53752 |
| Melting Point | 215 °C | 419 °F | Kofler |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 179 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 179 |
| Vicat Softening Point | 200 °C | 392 °F | 50 N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Stufe; IEC 707 |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Stufe; IEC 707 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 10 ohm-cm | <= 10 ohm-cm | IEC 93 |
| Surface Resistance | <= 20 ohm | <= 20 ohm | ISO 3915 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium to High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 105-71 Calcined Aluminum Oxide
- Samsung Cheil Industries Infino® XP-2165MC PPS
- Teknor Apex Monprene® MP-1776A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- A. Schulman POLYFORT™ FXP 1245U UV Stable Copolymer Polypropylene
- Chosun Refractories HSC-85AL Dense and High-Strength Castable, Credens
- 3M 4296T Adhesion Promoter
- ConocoPhillips 1 Milube® Grease 2100T NLGI No. 1
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR N339 Filler
- DuPont Bexloy® AXW604BK 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved