Styron EMERGEâ„¢ 4510-10 Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 4510-10 Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ PC 4510-10 advanced resin is a general purpose polycarbonate resin offering ignition resistance, heat resistance and excellent toughness. Applications: Consumer Electronics and Information Technology Equipment Computer and Business Equipment Portable Electronics Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 71.0 MPa | 10300 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Elongation at Break | 150 % | 150 % | 0.125 in, injection molded, unannealed; ASTM D638 |
| Tensile Modulus | 2.30 GPa | 334 ksi | 0.125 in, injection molded, unannealed; ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 0.125 in, injection molded, unannealed; ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm | 17.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | 0.157 in, annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | 0.157 in, unannealed; ASTM D648 |
| 138 °C | 280 °F | 0.157 in, annealed; ASTM D648 | |
| Vicat Softening Point | 146 °C | 295 °F | 50°C/hr, 50N; ASTM D1525 |
| Flammability, UL94 | V-2 | V-2 | 0.0625 in |
| V-2 | V-2 | 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 288 - 316 °C | 550 - 601 °F | |
| Mold Temperature | 71.0 - 104 °C | 160 - 219 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R7542X Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kinetics MIM 17-4PH Stainless Steel (H900 Condition)
- Momentive Performance Materials TUFELâ„¢ II 94505 Low Volatile Extrusion Heat Cured Rubber
- LG Chemical LUPOL GP3156F Flame Retardant PP
- Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F)
- SABIC Innovative Plastics Ultem 2313 PEI (Asia Pacific)
- Cytec Thornel® T-300 6K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- 3D Systems Accura® Xtreme Plastic for SLA® Systems
- Caplinq LINQTAPE™ PIT1A
Copyright © lookpolymers.com All Rights Reserved