ExxonMobil LDPE LD 302.56 Low Density Polyethylene Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer	Exxon Chemical
Trade Name	LDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LDPE LD 302.56 Low Density Polyethylene Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact strength, good heat sealability and good low temperature properties.Availability: Latin America, North America and South America Additive: Antiblock: 3000 ppmSlip: No Thermal Stabilizer: YesApplications: Coextrusion FilmsFoamsForm Fill and Seal PackagingFreezer FilmLamination FilmPoultry BagProduce BagsInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.924 g/cc	0.0334 lb/in³	ExxonMobil method
Vinyl Acetate Content	3.5 %	3.5 %	ExxonMobil Method
Melt Flow	1.3 g/10 min @Load 2.16 kg, Temperature 190 °C	1.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	3000 ppm	3000 ppm

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	190 %	190 %	ASTM D882
Film Elongation at Break, TD	580 %	580 %	ASTM D882
Puncture Energy	1.01 J	0.742 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	190 g	190 g	ASTM D1922
Elmendorf Tear Strength TD	110 g	110 g	ASTM D1922
Dart Drop Test	170 g	0.375 lb	ASTM D1709A
Film Tensile Strength at Break, MD	24.1 MPa	3500 psi	ASTM D882
Film Tensile Strength at Break, TD	23.4 MPa	3400 psi	ASTM D882
1% Secant Modulus, MD	145 MPa	21000 psi	ASTM D882
1% Secant Modulus, TD	172 MPa	25000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 221 °C	<= 430 °F	Peak Melting Point; ExxonMobil method

Optical Properties	Metric	English	Comments
Haze	6.5 %	6.5 %	ASTM D1003
Gloss	69 %	69 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Puncture Force	9 lbf	ExxonMobil Method