Network Polymers Softflex® 0615
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Network Polymers |
| Trade Name | Softflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Network Polymers Softflex® 0615.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.994 g/cc | 0.994 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 3.17 mm |
0.011 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 8.3 g/10 min @Load 1.00 kg, Temperature 235 °C |
8.3 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| 27 g/10 min @Load 5.00 kg, Temperature 200 °C |
27 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 48 - 58 | 48 - 58 | 10 second dwell; ASTM D2240 |
| 50 - 60 | 50 - 60 | Instantaneous; ASTM D2240 | |
| Tensile Strength, Yield | 7.79 MPa | 1130 psi | chs 20 in/min; ASTM D412 |
| Elongation at Break | 750 % | 750 % | ASTM D412 |
| 50% Modulus | 0.00138 GPa | 0.200 ksi | ASTM D412 |
| 100% Modulus | 0.00179 GPa | 0.260 ksi | ASTM D412 |
| 300% Modulus | 0.00448 GPa | 0.650 ksi | ASTM D412 |
| Flexural Modulus | 0.0150 GPa | 2.17 ksi | ASTM D790 |
| Gardner Impact | >= 36.2 J @Temperature -30.0 °C |
>= 26.7 ft-lb @Temperature -22.0 °F |
ASTM D5420 |
| Tear Strength | 28.4 kN/m | 162 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 0.192 | 0.192 | H22 Wheel 1000 g load/1000 cycles; ASTM D3389 |
| Compression Set | 18.4 % | 18.4 % | Method B, 22 hours at 25% deflection and 23°C; ASTM D395 |
| 67.9 % @Temperature 70.0 °C |
67.9 % @Temperature 158 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| 88.4 % @Temperature 100 °C |
88.4 % @Temperature 212 °F |
22 hours at 25% deflection; ASTM D395, Method B, | |
| Tensile Set | 9.3 % | 9.3 % | 100% strain; ASTM D412 |
Users viewing this material also viewed the following:
- Omya HYDROCARB® 90 HS Calcium Carbonate
- Shinkong Synthetic Fibers Shinite® T102G30 PET, 30% Glass Filled, Fire Retardant
- Techmer ES HiFill FR® PP FR-N X BKN001
- Solvay RHODAPEX® EST-65 Surfactant
- Teknor Apex Sinpolene MBW5335 Specialty Polystyrene
- A. Schulman PP 1467-01 Polypropylene Medium Impact Polypropylene
- ExxonMobil LDPE LD 650 Low Density Polyethylene Resin (European Grade)
- Colorite Polymers 9533 General Purpose Vinyl Compound
- DuPont Performance Polymers Crastin® SK695FR BK507 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- Sax Polymers SAXALEN PPH325GK20 Polypropylene Homopolymer, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved