Stratasys® ABS
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Stratasys |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stratasys® ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS is a strong, durable production-grade thermoplastic used across many industries. ABS is an ideal material for conceptual prototyping through design verification through direct digital manufacturing. The marriage of ABS with FDM technology gives you the ability to create Real Parts™ direct from digital files, in a variety of standard and custom colors. Refer to the FDM System Material Availability spec sheet for system availability and color options.Information provided by Stratasys®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 22.0 MPa | 3190 psi | Type 1, 2"/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.627 GPa | 236.0 ksi | ASTM D638 |
| Flexural Strength | 41.0 MPa | 5950 psi | ASTM D790 |
| Flexural Modulus | 1.834 GPa | 266.0 ksi | ASTM D790 |
| Izod Impact, Notched | 1.0678 J/cm | 2.0004 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.1356 J/cm | 4.0009 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 101 µm/m-°C @Temperature 20.0 °C |
56.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Glass Transition Temp, Tg | 104 °C | 219 °F | DSC (SSYS) |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.4 @Frequency 60.0 Hz |
2.4 @Frequency 60.0 Hz |
IEC 60250 |
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | IEC 60112 |
Users viewing this material also viewed the following:
- MV Labs FE165 K4Fe(CN)6·xH2O Potassium ferrocyanide(II) hydrate
- ExxonMobil Escorene® LD-770 Very High Flow EVA Resin for Specialty Applications (discontinued **)
- Mitsubishi Xantar® MX 1081 Polycarbonate-10% Glass Reinforced
- TIMCAL TIMREX® KS10 Primary Synthetic Graphite
- A. Schulman POLYFLAM™ FPP 1006 Talc Filled Homopolymer Polypropylene
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with DOP Plasticizer
- EMS-Grivory Grivory® CR 9 PA*
- CP-Polymer-Technik Wellamid® 6600 PA-66-HWL UL-Licensed Nylon 66, Flame Protection Grade V-2, Heat Stabilized, Dry
- A. Schulman ComAlloy Voloy® 411 Mineral Reinforced, PBT Alloy, Flame Retardant, UL
Copyright © lookpolymers.com All Rights Reserved