Category | Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE |
Manufacturer | Stellarchem |
Trade Name | |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Stellarchem AB-860LG TPE Compound.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.16 g/cc | 0.0419 lb/in³ | |
Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
Melt Flow | 7.44 g/10 min | 7.44 g/10 min | JIS K7210 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 66 | 66 | JIS K6301 |
Tensile Strength, Ultimate | 4.41 MPa | 640 psi | JIS K6301 |
Elongation at Break | 535 % | 535 % | JIS K6301 |
100% Modulus | 0.01764 GPa | 2.559 ksi | JIS K6301 |
300% Modulus | 0.00118 GPa | 0.171 ksi | JIS K6301 |
Tear Strength | 32.6 kN/m | 186 pli | JIS K6301-B |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 200 - 220 °C | 392 - 428 °F | Metering Temperature, Extrusion |
Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
160 - 180 °C | 320 - 356 °F | Extrusion | |
Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
180 - 200 °C | 356 - 392 °F | Transition, Extrusion | |
Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
220 - 230 °C | 428 - 446 °F | Extrusion | |
Nozzle Temperature | 220 - 230 °C | 428 - 446 °F | Injection Molding |
Die Temperature | 195 - 210 °C | 383 - 410 °F | Extrusion |
Melt Temperature | 180 - 230 °C | 356 - 446 °F | Injection Molding |
180 - 230 °C | 356 - 446 °F | Extrusion | |
Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
100 - 200 rpm | 100 - 200 rpm | Injection Molding |