Star Plastics PC/ABSQX7004 Molding Grade PC/ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PC/ABSQX7004 Molding Grade PC/ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 260 °C |
10 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | ASTM D638 |
| Tensile Modulus | 2.28 GPa | 330 ksi | ASTM D638 |
| Flexural Yield Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 6.14 J/cm | 11.5 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | unannealed, .125in; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 282 °C | 460 - 540 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 260 - 304 °C | 500 - 580 °F | |
| Nozzle Temperature | 260 - 304 °C | 500 - 580 °F | |
| Melt Temperature | 260 - 304 °C | 500 - 580 °F | |
| Mold Temperature | 73.9 - 102 °C | 165 - 215 °F | |
| Drying Temperature | 87.8 - 110 °C | 190 - 230 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Screw Speed | 25 - 75 rpm | 25 - 75 rpm |
Users viewing this material also viewed the following:
- Nylene® 9633 , 33% Glass Reinforced Nylon 6,6/6
- Owens Corning Glass Fiber Reinforced Nylon 6, 30 wt.% glass
- Termopol Termoton® K2GA3060A TPE Compound, based on SEBS and Polyolefins
- Honeywell Capran® Oxyshield™ OXTR (Retortable Grade, 1.0 mil) Monoaxially Oriented Co-Extruded Nylon 6/EVOH/Nylon 6 Clear Film
- Micropol Microlin ML21 Linear Polyethylene Rotational Molding Powder
- A. Schulman POLYFORT™ PX 1042
- A. Schulman POLYFLAM™ RCP 500 C
- Crucible Steel Cru-Wear® Tool Steel
- Barlog Plastics KEBATER A1100 PBT/PC unreinforced, high impact
- Adell BR-38 Nylon 6, 40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved