Star Plastics PC/ABSFR9002 Molding Grade PC/ABSFR

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Star Plastics, Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Star Plastics PC/ABSFR9002 Molding Grade PC/ABSFR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Star Plastics, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 17 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 17 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 61.4 MPa
8900 psi
ASTM D638
Tensile Modulus 2.55 GPa
370 ksi
ASTM D638
Flexural Yield Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 2.59 GPa
375 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
73°F, 0.125 in.; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 93.3 °C
200 °F
unannealed, .125in; ASTM D648
Flammability, UL94 V-0
V-0
.062in
Processing Properties Metric English Comments
Rear Barrel Temperature 232 - 260 °C
450 - 500 °F
Middle Barrel Temperature 246 - 274 °C
475 - 525 °F
Front Barrel Temperature 246 - 288 °C
475 - 550 °F
Nozzle Temperature 246 - 288 °C
475 - 550 °F
Melt Temperature 246 - 288 °C
475 - 550 °F
Mold Temperature 57.2 - 85.0 °C
135 - 185 °F
Drying Temperature 82.2 - 110 °C
180 - 230 °F
Dry Time 3 - 4 hour
3 - 4 hour
Back Pressure 0.172 - 0.689 MPa
25.0 - 100 psi
Screw Speed 25 - 75 rpm
25 - 75 rpm