- Special Metals MONEL® Alloy K-500
Special Metals MONEL® Alloy K-500
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | MONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals MONEL® Alloy K-500.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A precipitation-hardenable nickel-copper alloy that combines the corrosion resistance of MONEL alloy 400 with greater strength and hardness. It also has low permeability and is nonmagnetic to under -150°F (-101°C). Used for pump shafts, oil-well tools and instruments, doctor blades and scrapers, springs, valve trim, fasteners, and marine propeller shafts. Standard product forms are round, hexagon, flats, forging stock, pipe, tube, plate, sheet, strip, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 860 MPa @Temperature 425 °C |
125000 psi @Temperature 797 °F |
Precipitation Hardened prior to test |
| 1100 MPa @Temperature 23.0 °C |
160000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 790 MPa @Strain 0.200 % |
115000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 630 MPa @Strain 0.200 %, Temperature 425 °C |
91400 psi @Strain 0.200 %, Temperature 797 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 25 % | 25 % | Precipitation Hardened |
| 12 % @Temperature 425 °C |
12 % @Temperature 797 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.7 µm/m-°C @Temperature 20.0 - 100 °C |
7.61 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
| Thermal Conductivity | 17.5 W/m-K | 121 BTU-in/hr-ft²-°F | |
| Melting Point | 1315 - 1350 °C | 2399 - 2460 °F | |
| Solidus | 1315 °C | 2399 °F | |
| Liquidus | 1350 °C | 2460 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 2.3 - 3.15 % | 2.3 - 3.15 % | |
| Carbon, C | <= 0.25 % | <= 0.25 % | |
| Copper, Cu | 27 - 33 % | 27 - 33 % | |
| Iron, Fe | <= 2.0 % | <= 2.0 % | |
| Manganese, Mn | <= 1.5 % | <= 1.5 % | |
| Nickel, Ni | >= 63 % | >= 63 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.35 - 0.85 % | 0.35 - 0.85 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000615 ohm-cm | 0.0000615 ohm-cm | |
| Magnetic Permeability | 1.002 | 1.002 | at 200 oersted (15.9 kA/m) |
| Curie Temperature | -65.0 °C | -85.0 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Europe-Africa-Middle East)
- LG Chemical R120 EPS, Flame Retardant
- Lavergne VYPET VNT 630 FR PET 30% Glass Reinforced, Flame Retardant
- SYNTHOS Forsan® 548 Acrylonitrile Butadiene Styrene (ABS)
- Spartech Polypedic F High Density Polyethylene
- Styron CALIBREâ„¢ 303-10 Polycarbonate
- Unitika A1025NO PA6, Flame Retardant, Conditioned
- Aclo Accutech Polypropylene Copolymer CP0436W10L1 Wollastonite Reinforced
- Atom Adhesives AA-GREASE 04 Epoxy Adhesive
- BASF Procom® X10S 773 Polypropylene
Copyright © lookpolymers.com All Rights Reserved