- Chosun Refractories CTL ARS Monolithic Refractories for Ladle and Tundish
Chosun Refractories CTL ARS Monolithic Refractories for Ladle and Tundish
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories CTL ARS Monolithic Refractories for Ladle and Tundish.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.01010 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
1.466 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.02560 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
3.714 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 32.2 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
4670 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 98.1 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
14200 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | 0.00 % <br>@Temperature 110 °C,<br> Time 86400 sec |
0.00 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.18 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.18 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 97 % | 97 % | |
| MgO | 1.0 % | 1.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Vibrating | |
| Main Applications | Wall | |
| Water Required for Casting(%) | 103 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 14 HI TS PA66, 14% glass fibre, improved strength
- Chevron Phillips MarFlex® 1010 LDPE Extrusion Coating Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 1105-8053/EM/BL PEEK, with glass fiber, easy flowing
- Teknor Apex APEX® 80131 Polyvinyl Chloride, Flexible
- Hexcel® HexPly® 1454 125°C Curing Epoxy Matrix
- Cossa Polimeri ESTABLEND PSA 6600 PC / ASA Blend
- DuPont Performance Polymers Crastin® 6130 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- BASF Ultramid® B3WG6 30% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved