- Special Metals INCONEL® 690 Nickel Superalloy, Hot Rolled Flat, 0.5 x 2.0 inch (13 x 51 mm)
Special Metals INCONEL® 690 Nickel Superalloy, Hot Rolled Flat, 0.5 x 2.0 inch (13 x 51 mm)
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 690 Nickel Superalloy, Hot Rolled Flat, 0.5 x 2.0 inch (13 x 51 mm).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Composition adjustments for nuclear applications: 28-31 Cr; 0.04 max C; 0.10 max Co.Tensile strength (ultimate and yield) and elongation values reported here are typical for Hot Rolled Flat, 0.5 x 2.0 inch (13 x 51 mm). Other property values are typical of INCONEL® alloy 690.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.19 g/cc | 0.296 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 703 MPa | 102000 psi | |
| Tensile Strength, Yield | 352 MPa @Strain 0.200 % |
51000 psi @Strain 0.200 % |
|
| Elongation at Break | 46 % | 46 % | |
| Modulus of Elasticity | 211 GPa | 30600 ksi | |
| Poissons Ratio | 0.289 | 0.289 | |
| Shear Modulus | 81.8 GPa | 11900 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.06 µm/m-°C @Temperature 24.0 - 100 °C |
7.811 µin/in-°F @Temperature 75.2 - 212 °F |
Mean |
| 14.53 µm/m-°C @Temperature 24.0 - 300 °C |
8.072 µin/in-°F @Temperature 75.2 - 572 °F |
Mean | |
| 15.19 µm/m-°C @Temperature 24.0 - 500 °C |
8.439 µin/in-°F @Temperature 75.2 - 932 °F |
Mean | |
| 17.41 µm/m-°C @Temperature 20.0 - 1000 °C |
9.672 µin/in-°F @Temperature 68.0 - 1830 °F |
Mean, extrapolated | |
| Specific Heat Capacity | 0.450 J/g-°C | 0.108 BTU/lb-°F | |
| Thermal Conductivity | 13.5 W/m-K | 93.7 BTU-in/hr-ft²-°F | |
| Melting Point | 1343 - 1377 °C | 2449 - 2511 °F | |
| Solidus | 1343 °C | 2449 °F | |
| Liquidus | 1377 °C | 2511 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.050 % | <= 0.050 % | |
| Chromium, Cr | 27 - 31 % | 27 - 31 % | |
| Copper, Cu | 0.50 % | 0.50 % | |
| Iron, Fe | 7.0 - 11 % | 7.0 - 11 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.15 % | <= 0.15 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0001148 ohm-cm | 0.0001148 ohm-cm | |
| Magnetic Permeability | 1.001 | 1.001 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- MV Labs DY800 Dy2O3 Dysprosium oxide
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, 350ºF Cure Temperature
- SABIC Innovative Plastics LNP LUBRICOMP UAL23AS PPA (Europe-Africa-Middle East)
- Struktol ZINC STEARATE
- Sichuan Deyang Haton® hMR61LC1 Polyphenylene Sulfide, Glass & Mineral Reinforced
- Polyram PlusTek PA340S4 Nylon 66 for Injection Molding, 20% Glass-Beads Reinforced
- Fainplast Compounds PM 55/K Flexible PVC, Lead Free
- Aaron Industries AAROPRENE® GFN 6613 Glass Filled Nylon 6/6
- BLUESTAR LXS 112 PPE-PS
Copyright © lookpolymers.com All Rights Reserved