- Spartech PP5120 Talc Filled Homopolymer
Spartech PP5120 Talc Filled Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech PP5120 Talc Filled Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc @Temperature 22.8 °C |
1.04 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.1 MPa | 4800 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Modulus | 1.90 GPa | 275 ksi | secant; ASTM D790 |
| 2.48 GPa | 360 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm @Temperature 22.8 °C |
0.600 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 1.36 J @Temperature 22.8 °C |
1.00 ft-lb @Temperature 73.0 °F |
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 47 % | 47 % | 60°; ASTM D523 |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Cogegum® AFR/765 Polyolefin, Unspecified (Unverified Data**)
- Polymer Resources PC/ABS-FR1-[color]-UV Flame Retardant PC/ABS Alloy, UV-stabilized
- Ineos Nova 5511 High Impact Polystyrene
- Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick
- Isoflon Tisoflon® 10S Silicone Coated Glass Fabric
- Dr. D. Mueller Flexiso® DMD FI 14010 00100 Polyester Electrical Insulation
- Ensinger TECASINT 1031 Polyimide, 40% Graphite Filled (PI)
- Master Bond EP21TP-2 Oil And Fuel Resistant Polysulfide Based Adhesive System
- H.C. Starck Amperit® 525.2 Sintered Tungsten Carbide - Cobalt (WC-Co) 83-17
Copyright © lookpolymers.com All Rights Reserved