Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH0
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamides PA66, reinforced with 35% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V35 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade in commonly used in the automotive industry of engine components, such as inlet manifolds, air ducts, engine cover, and various housing and liquid containers.This product is available in natural, black and grey.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183-A |
| Water Absorption | 0.75 % | 0.75 % | 24 hours in water at 23°C; ISO 62. |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 210 MPa | 30500 psi | ISO 527 |
| Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 11.4 GPa | 1650 ksi | ISO 527 |
| Flexural Yield Strength | 286 MPa | 41500 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact Resistance | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 1.35 J/cm² | 6.42 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 22.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 |
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 243-1 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F |
Users viewing this material also viewed the following:
- Permabond HH120 Anaerobic Threadlocker
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler
- LyondellBasell Alathon® L5845 High Density Polyethylene
- Indium Corp. Indalloy 193 Silver Solder Alloy
- Westlake Hifor Clear SC74580 Linear Low Density Polyethylene
- A. Schulman SCHULINK® X XL350 Cross-Linkable, High Density Polyethylene
- A. Schulman PP 1248-01 Polypropylene High-Flow Homopolymer Polypropylene
- ExxonMobil Mobil Clean 5W-30 Motor Oil
- Dynasol Solprene® 233 Medium CIS Polybutadiene
Copyright © lookpolymers.com All Rights Reserved