Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH0
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is commonly used in the automotive industry for engine components, such as water tanks, degassing and liquid containers, engine covers, and various housing.This product is available in natural, black and in colors on request.Glow wire test thick. 1,6 mm, IEC 695-2-1, is 700°C.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183-A |
| Water Absorption | 0.80 % | 0.80 % | 24 hours in water at 23°C; ISO 62. |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 190 MPa | 27600 psi | ISO 527 |
| Tensile Strength, Yield | 190 MPa | 27600 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 |
| Flexural Yield Strength | 260 MPa | 37700 psi | ISO 178 |
| Flexural Modulus | 8.40 GPa | 1220 ksi | ISO 178 |
| Izod Impact Resistance | 1.10 J/cm² | 5.24 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
13.9 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 |
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 5.00e+14 ohm-cm | 5.00e+14 ohm-cm | IEC 93 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 243-1 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 SG15 Nylon 6.6 for injection molding, 15% mineral filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.5 PHR Sulfur
- Kazanorgsintez PE2NT 18-11 Linear Low Density Polyethylene
- Lucent Polymers PC-FR0 Polycarbonate, Flame Resistant
- Styrolution Terluran® HI-10 ABS
- Silon TA 2347 HD Orange Catalyst Masterbatch
- A. Schulman PP 828-31 Polypropylene Black Molding Grade Impact Polypropylene
- Ametek High Purity Nickel Strip 899L Hard
- G-2706 Styrene-based Biomedical Elastomer
- Aclo Accutech TPO TPO030T9V Paintable Grade
Copyright © lookpolymers.com All Rights Reserved