- Solvay TECHNYLSTARâ„¢ SX 216 V50 PA6, 50% glass filled, DRY
Solvay TECHNYLSTARâ„¢ SX 216 V50 PA6, 50% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ SX 216 V50 PA6, 50% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYLSTAR Polyamide, reinforced with 50% of glass fiber, characterized by a high fluidity of the melt, for injection molding.Available in: Asia Pacific, Europe and North America Product Applications: TECHNYLSTAR TM SX 216 V50 is suitable for all applications where a high rigidity is required. Due to its outstanding flow properties, the material easily fills the mould and the surface aspect of the finished part is excellent. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183/A |
| Water Absorption | 0.72 % @Temperature 23.0 °C, Time 86400 sec |
0.72 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0072 cm/cm | 0.0072 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0023 cm/cm | 0.0023 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0032 cm/cm | 0.0032 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527 Type 1A |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 Type 1A |
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527 Type 1A |
| Flexural Modulus | 15.5 GPa | 2250 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |
| Front Barrel Temperature | 240 - 245 °C | 464 - 473 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.15 % | <= 0.15 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 235-240°C |
Users viewing this material also viewed the following:
- Nye Lubricants 140B (SO) Synthetic Oil
- Samsung Cheil Industries Starex® HF-5330S ASA, Unreinforced (discontinued **)
- Taiwan Sheen Soon Sheenthane® A8510H TPU for Ink
- SABIC Innovative Plastics LNP THERMOCOMP C7410 PC+ABS (Asia Pacific)
- Techmer ES Plastiblend® TPX-HTN-000AB 15% Glass Filled
- A. Schulman SUPERLINEAR™ XL 0370 Rotational Molding Resin
- ExxonMobil Bicor® 50 LBW OPP Film
- Ashley Polymers Ashlene® P106 PBT Polyester
- Colorite Polymers 7075 General Purpose Vinyl Compound
- DuPont Performance Polymers Zytel® HTN FE350064 BK544 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved