Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYL® R |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® R AR 130/GF Nylon 66, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® AR 130/GF is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in black color. Benefits: The product offers a good combination between thermal and mechanical properties.Available in: Europe Regulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC This grade complies with RoHS directive 2002/95/EC Unless specified, this grade is not suitable for food contact, medical devices or toy applicationsApplications: It is used in a wide variety of industries for applications without severe impact resistance requirements, such as fans and shrouds components in automotive.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527 Type 1A |
| Tensile Modulus | 9.20 GPa | 1330 ksi | ISO 527 Type 1A |
| Flexural Strength | 227 MPa | 32900 psi | ISO 178 |
| Flexural Modulus | 8.25 GPa | 1200 ksi | ISO 178 |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | ISO 180/1U |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C | |
| Mixing Zone | 280-290°C |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3880H TPE, PP Overmold or Standalone use
- PSM Industries Pacific Sintered Metals Bronze BT-121-R Powdered Metal
- SPS Guang Zhou REMATâ„¢ 5003RM5A Flame-retarded PP masterbatch
- ExxonMobil Teresstic 68
- BASF Ultramid® 8253 PA6 (Dry)
- IRPC Polimaxx Polene 2563PCX TA6 Polypropylene Compound
- Shinkong Synthetic Fibers Shinite® D201 PBT
- EG80A Polyurethane-based Biomedical Elastomer
- DuPont Performance Polymers Crastin® LW9330 NC010 PBT (Unverified Data**)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 30 PHR N550 (FEF) Filler
Copyright © lookpolymers.com All Rights Reserved