Solvay TECHNYLÂ® C 246SI V11 PA6, 11% glass filled, DRY

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled
Manufacturer	Solvay
Trade Name	Technyl®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay TECHNYLÂ® C 246SI V11 PA6, 11% glass filled, DRY.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Polyamide 6, reinforced with 11% of glass fiber, with high impact resistance, for injection molding.Available in: Asia PacificProduct Applications: TECHNYLÂ® C 246SI V11 has good mechanical properties and impact strength at low temperature. This grade is widely used for: ski boot parts. This product is available in natural color and colors in request.Information provided by Rhodia, Rhodia has been acquired by Solvay.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/inÂ³	ISO 1183/A

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	90.0 MPa	13100 psi	ASTM D638
Elongation at Break	7.0 %	7.0 %	ASTM D638
Flexural Strength	135 MPa	19600 psi	ASTM D790
Flexural Modulus	4.10 GPa	595 ksi	ASTM D790
Izod Impact, Notched	1.95 J/cm	3.65 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	222 Â°C	432 Â°F	ISO 11357
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Processing Properties	Metric	English
Feed Temperature	250 - 280 Â°C	482 - 536 Â°F
Front Barrel Temperature	260 - 290 Â°C	500 - 554 Â°F
Mold Temperature	70.0 - 90.0 Â°C	158 - 194 Â°F
Drying Temperature	80.0 Â°C	176 Â°F
Moisture Content	<= 0.20 %	<= 0.20 %

Descriptive Properties	Value	Comments
Compression Zone	250-280Â°C