Solvay Specialty Polymers Veradel® AG-320 Polyethersulfone (PESU) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Veradel® AG-320 Polyethersulfone (PESU) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Veradel AG-320 is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the material, while maintaining most of its other basic characteristics. The combination of structural properties and cost effectiveness make this resin an attractive alternative to metals in many engineering applications. This grade was formerly marketed as Radel® A PESU - Natural: Veradel AG-320 NTInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	1.51 g/cc	1.51 g/cc	ASTM D792
Filler Content	20 %	20 %	Glass Fiber Reinforcement
Water Absorption	0.45 % @Time 86400 sec	0.45 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0040 cm/cm	0.0040 in/in	ASTM D955
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 343 °C	6.0 g/10 min @Load 4.76 lb, Temperature 649 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	109 MPa	15800 psi	ASTM D638
Elongation at Break	3.2 %	3.2 %	ASTM D638
Tensile Modulus	5.69 GPa	825 ksi	ASTM D638
Flexural Strength	162 MPa	23500 psi	ASTM D790
Flexural Modulus	6.55 GPa	950 ksi	ASTM D790
Izod Impact, Notched	0.590 J/cm	1.11 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	31.0 µm/m-°C @Thickness 3.18 mm	17.2 µin/in-°F @Thickness 0.125 in	ASTM D696
Deflection Temperature at 1.8 MPa (264 psi)	214 °C @Thickness 3.18 mm	417 °F @Thickness 0.125 in	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 0.787 mm	V-0 @Thickness 0.0310 in	UL 94

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.84 @Frequency 1000 Hz	3.84 @Frequency 1000 Hz	ASTM D150
	3.84 @Frequency 60.0 Hz	3.84 @Frequency 60.0 Hz	ASTM D150
	3.88 @Frequency 1.00e+6 Hz	3.88 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	17.0 kV/mm	432 kV/in	ASTM D149
Dissipation Factor	0.0015 @Frequency 60.0 Hz	0.0015 @Frequency 60.0 Hz	ASTM D150
	0.0018 @Frequency 1000 Hz	0.0018 @Frequency 1000 Hz	ASTM D150
	0.0081 @Frequency 1.00e+6 Hz	0.0081 @Frequency 1.00e+6 Hz	ASTM D150

Processing Properties	Metric	English
Melt Temperature	343 - 399 °C	649 - 750 °F
Mold Temperature	149 - 163 °C	300 - 325 °F
Drying Temperature	149 - 177 °C	300 - 351 °F
Dry Time	2.50 - 4.00 hour	2.50 - 4.00 hour
Back Pressure	0.345 - 0.689 MPa	50.0 - 99.9 psi

Descriptive Properties	Value	Comments
Agency Ratings	NSF 51	Maximum Temperature of Use: 190°C (375°F)
Appearance	Colors Available
	Natural Color
Automotive Specifications	FORD WSK-M4D773-A2 Color: BK184 Black
	FORD WSK-M4D773-A2 Color: NT Natural
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Acid Resistant
	Flame Retardant
	Food Contact Acceptable
	Good Adhesion
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Strength
	Good Thermal Stability
	Good Toughness
	High Heat Resistance
	High Rigidity
	High Tensile Strength
	Hydrolysis Resistant
	Medium Flow
	Medium Molecular Weight
Forms	Pellets
Generic	PESU
Injection Rate	Fast
Processing Method	Injection Molding
RoHS Compliance	RoHS Compliant
Screw Compression Ratio	2.0:1.0
Uses	Appliance Components
	Appliances
	Automotive Electronics
	Batteries
	Business Equipment
	Electrical Parts
	Electrical/Electronic Applications
	Food Service Applications
	Industrial Applications
	Metal Replacement
	Microwave Cookware
	Plumbing Parts
	Valves/Valve Parts