Eastman Tenite 371A-08 Cellulose Acetate Propionate  (discontinued **)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Tenite 371A-08 Cellulose Acetate Propionate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
8% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
Linear Mold Shrinkage, Flow 0.0020 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0020 - 0.0060 in/in

@Thickness 0.126 in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 38.0 MPa
5510 psi
50 mm/min
Elongation at Break 36 %
36 %
Elongation at Yield 4.1 %
4.1 %
Tensile Modulus 1.85 GPa
268 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 0.580 J/cm²
2.76 ft-lb/in²
0.440 J/cm²

@Temperature -30.0 °C
 2.09 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 89.0 µm/m-°C

@Temperature 20.0 °C
 49.4 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 122 µm/m-°C

@Temperature 20.0 °C
 67.8 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C
205 °F
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Vicat Softening Point 96.0 °C
205 °F
Glass Transition Temp, Tg 111 °C
232 °F
Processing Properties Metric English Comments
Melt Temperature 230 - 245 °C
446 - 473 °F